Effect of Light-Cured Resin Cement Application on Translucency of Ceramic Veneers and Light Transmission of LED Polymerization Units.

To evaluate the effect of light-cured resin cement application based on etching and silanization on the translucent property of ceramic veneers in different thicknesses, testing the hypothesis that the surface treatment and subsequent resin cement application could influence the translucency of ceramic veneers. The relationship between translucency of ceramic veneers and light transmission irradiated by LED polymerization units was also determined. 40 specimens (10 mm diameter) were fabricated from IPS e.max Press HT A2 ceramic ingots, and polished to 0.3 ± 0.01 mm, 0.5 ± 0.01 mm, 0.7 ± 0.01 mm, 1.0 ± 0.01 mm, and 1.5 ± 0.01 mm thick (n = 8/group). One surface of each disc was etched with HF acid, silanized with Monobond-S, and applied with a light-cured resin cement (Variolink N Transparent Base). Before and after the above procedure, the total luminous transmittance (τ) of all specimens was assessed by a spectrophotometer in a wavelength range of 380-780 nm. A handheld radiometer was used to measure the light intensity irradiated by three LED polymerization units. Light transmission (LT) through ceramic specimens after resin cement application was calculated. Data were statistically analyzed using two-way ANOVA (p = 0.05) and Tukey's test. The correlation between translucency (τ) of ceramic veneers after resin cement application and light transmission (LT) of curing units was statistically evaluated using Spearman correlation test (p = 0.05). With the increase of ceramic thickness, the transmittance decreased significantly (p < 0.05). For the 0.3-mm, 0.5-mm, and 0.7-mm-thick groups, the transmittance of ceramic specimens was statistically significantly lower after resin cement application (p < 0.05). The r value of Bluephase C8 was 0.988, 0.977 for Bluphase, and 0.883 for Bluephase 20i, indicating that the light transmission (LT%) was positively correlated to the translucency of ceramic veneers, regardless of the type of curing units. After the light-cured resin cement application based on etching and silanization, the ceramic veneers (less than 0.7-mm thick) were less translucent, and the translucency decreased when the thickness increased. Because of the lower translucency of ceramic veneers, the light intensity of LED units transmitted to resin layer would decrease when curing.

Informations de copyright

© 2018 by the American College of Prosthodontists.