Strain-engineering Mott-insulating La
Journal
Nature communications
ISSN: 2041-1723
Titre abrégé: Nat Commun
Pays: England
ID NLM: 101528555
Informations de publication
Date de publication:
19 02 2019
19 02 2019
Historique:
received:
31
07
2018
accepted:
20
01
2019
entrez:
21
2
2019
pubmed:
21
2
2019
medline:
21
2
2019
Statut:
epublish
Résumé
The transition temperature T
Identifiants
pubmed: 30783084
doi: 10.1038/s41467-019-08664-6
pii: 10.1038/s41467-019-08664-6
pmc: PMC6381167
doi:
Types de publication
Journal Article
Research Support, Non-U.S. Gov't
Langues
eng
Pagination
786Références
Nat Mater. 2013 Nov;12(11):1019-23
pubmed: 23913170
Sci Rep. 2016 Mar 11;6:22715
pubmed: 26964524
Sci Adv. 2016 Dec 07;2(12):e1601646
pubmed: 27957540
J Appl Crystallogr. 2018 Oct 18;51(Pt 6):1745-1751
pubmed: 30546291
Phys Rev Lett. 2001 Jun 4;86(23):5377-80
pubmed: 11384502
Phys Rev Lett. 2010 Oct 15;105(16):167002
pubmed: 21230997
J Synchrotron Radiat. 2010 Sep;17(5):631-43
pubmed: 20724785
Phys Rev Lett. 2010 Jul 30;105(5):057003
pubmed: 20867949
Nat Commun. 2013;4:2559
pubmed: 24096628
Phys Rev B Condens Matter. 1994 Feb 1;49(6):4163-4175
pubmed: 10011314
Nat Commun. 2018 Mar 6;9(1):972
pubmed: 29511188
Sci Rep. 2016 May 12;6:25335
pubmed: 27174799
Phys Rev Lett. 2010 Dec 10;105(24):247001
pubmed: 21231553
Phys Rev Lett. 2005 Aug 12;95(7):077001
pubmed: 16196815
Phys Rev Lett. 2003 Aug 1;91(5):057002
pubmed: 12906624
Nat Commun. 2014 Feb 28;5:3314
pubmed: 24577074