Silicoaluminophosphate (SAPO)-Templated Activated Carbons.
Journal
ACS omega
ISSN: 2470-1343
Titre abrégé: ACS Omega
Pays: United States
ID NLM: 101691658
Informations de publication
Date de publication:
30 Jun 2019
30 Jun 2019
Historique:
received:
15
01
2019
accepted:
15
05
2019
entrez:
29
8
2019
pubmed:
29
8
2019
medline:
29
8
2019
Statut:
epublish
Résumé
Microporous activated carbon was prepared by depositing and pyrolyzing propylene within the microporous voids of SAPO-37 and subsequently removing the template by a treatment with HCl and NaOH. The carbon had a high surface area and large micropore and ultramicropore volumes. The yield, crystallinity, morphology, and adsorption properties compared well with those of a structurally related zeolite-Y-templated carbon. No HF was needed to remove the SAPO-37 template in contrast to the zeolite Y template, which could be of industrial importance.
Identifiants
pubmed: 31460079
doi: 10.1021/acsomega.9b00135
pmc: PMC6648489
doi:
Types de publication
Journal Article
Langues
eng
Pagination
9889-9895Déclaration de conflit d'intérêts
The authors declare no competing financial interest.
Références
Nature. 2002 Jun 20;417(6891):813-21
pubmed: 12075343
J Microsc. 2003 Apr;210(Pt 1):53-9
pubmed: 12694416
Chem Commun (Camb). 2006 Mar 7;(9):991-3
pubmed: 16491186
J Phys Chem B. 2006 Sep 21;110(37):18424-31
pubmed: 16970467
Langmuir. 2007 May 8;23(10):5477-84
pubmed: 17429989
Phys Chem Chem Phys. 2007 Nov 28;9(44):5919-27
pubmed: 17989800
J Colloid Interface Sci. 2010 Feb 15;342(2):467-73
pubmed: 19919862
J Am Chem Soc. 2011 Feb 9;133(5):1165-7
pubmed: 21207996
Chem Commun (Camb). 2013 Dec 28;49(100):11737-9
pubmed: 24202181
Langmuir. 2014 Jan 14;30(1):297-307
pubmed: 24359449
Nature. 2016 Jul 7;535(7610):131-5
pubmed: 27362224
Chem Sci. 2016 Jun 1;7(6):3564-3568
pubmed: 29997848