Mechanical properties and metallurgical features of new and ex vivo used Reciproc Blue and Reciproc.
cyclic fatigue
differential scanning calorimetry
focused ion beam analysis
heat treatment
metallographic analysis
usage-induce degradation
Journal
International endodontic journal
ISSN: 1365-2591
Titre abrégé: Int Endod J
Pays: England
ID NLM: 8004996
Informations de publication
Date de publication:
Feb 2020
Feb 2020
Historique:
received:
28
05
2019
accepted:
30
08
2019
pubmed:
7
9
2019
medline:
11
1
2020
entrez:
7
9
2019
Statut:
ppublish
Résumé
To compare the mechanical properties and metallurgic features of new and used Reciproc Blue and Reciproc instruments. A total of 120 R25 Reciproc Blue and R25 Reciproc instruments were used. The morphological, chemical, mechanical, thermal and phase composition characteristics of new and ex vivo used files were investigated by scanning electron microscopy (FEG-SEM) with energy dispersive X-ray spectroscopy (EDS), focused ion beam analysis (FIB), micro-Raman spectroscopy, FEG-SEM metallography, X-ray diffraction (XRD), differential scanning calorimetry (DSC) and indentation tests. Usage-induce degradation was evaluated. Ten new and ten used instruments per type were run until fracture occurred in a stainless steel artificial canal (60° angle of curvature, 4-mm radius). Time to fracture and the length of the fractured fragment were recorded. Torque and angle of rotation at failure of ten new and ten used instruments for each type were measured according to ISO 3630-1. The fracture surface of each fragment was examined. Two-way analyses of variance was used to analyse the data statistically (α-level 0.05). SEM analysis revealed microcracks near the tip on both files after ex vivo usage tests. FIB imaging and micro-Raman spectroscopy confirmed the presence of an oxide layer on the Reciproc Blue surface. There was no thinning of the coating after use. XRD revealed a reduction of martensite and R-phase in Reciproc Blue after use. DSC analysis revealed different transformation temperatures for the instruments analysed. Reciproc Blue was significantly more flexible than Reciproc for both new and used samples (P < 0.05), and they were significantly more resistant to cyclic fatigue than Reciproc (P < 0.05). Ex vivo usage reduced the fatigue resistance of both files. Torsional resistance of Reciproc and Reciproc Blue was not reduced by simulated use (P > 0.05). The thermal treatment of Reciproc Blue was associated with a finer structure with smaller grains than Reciproc, which increased its fracture resistance and was also responsible for its reduced hardness and lower elastic modulus. Both files were safe during ex vivo usage in severely curved canals.
Substances chimiques
Titanium
D1JT611TNE
Types de publication
Journal Article
Langues
eng
Pagination
250-264Informations de copyright
© 2019 International Endodontic Journal. Published by John Wiley & Sons Ltd.
Références
Alfawaz H, Alqedairi A, Alsharekh H, Almuzaini S, Jamleh A (2018) Effects of sodium hypochlorite concentration and temperature on the cyclic fatigue resistance of heat-treated nickel-titanium rotary instruments. Journal of Endodontics 44, 1563-6.
Arens FC, Hoen MM, Steiman HR, Dietz GC Jr (2003) Evaluation of single-use rotary nickel-titanium instruments. Journal of Endodontics 29, 664-6.
ASM Handbook Vol. 12 (1987) Fractography. Materials Park, OH: ASM International.
Callister WD, Rethwisch DG (2015) Fundamentals of Materials Science and Engineering: An Integrated Approach, 5th edn. Hoboken, USA: Wiley.
De-Deus G, Barino B, Marins J, Magalhães K, Thuanne E, Kfir A (2012) Self-adjusting file cleaning-shaping-irrigation system optimizes the filling of oval-shaped canals with thermoplasticized gutta-percha. Journal of Endodontics 38, 846-9.
De-Deus G, Silva EJ, Vieira VT et al. (2017) Blue thermomechanical treatment optimizes fatigue resistance and flexibility of the Reciproc files. Journal of Endodontics 43, 462-6.
Elnaghy AM, Elsaka SE (2015) Torsion and bending properties of OneShape and WaveOne instruments. Journal of Endodontics 41, 544-7.
Elsaka SE, Elnaghy AM, Badr AE (2017) Torsional and bending resistance of WaveOne Gold, Reciproc and Twisted File Adaptive instruments. International Endodontic Journal 50, 1077-83.
Gao Y, Gutmann JL, Wilkinson K, Maxwell R, Ammon D (2012) Evaluation of the impact of raw materials on the fatigue and mechanical properties of ProFile Vortex rotary instruments. Journal of Endodontics 38, 398-401.
Generali L, Righi E, Todesca MV, Consolo U (2014) Canal shaping with WaveOne Reciprocating files: influence of operator experience on instrument breakage and canal preparation time. Odontology 102, 217-22.
Generali L, Borghi A, Lusvarghi L et al. (2019) Evauation of the usage.induced degradation of Genius and Reciproc nickel-titanium Reciprocating instruments. Odontology 107, 473-81.
Grande NM, Plotino G, Pecci R, Bedini R, Malagnino VA, Somma F (2006) Cyclic fatigue resistance and three-dimensional analysis of instruments from two nickel-titanium rotary systems. International Endodontic Journal 39, 755-63.
Grande NM, Ahmed HMA, Cohen S, Bukiet F, Plotino G (2015) Current assessment of Reciprocation in endodontic preparation: a comprehensive review - part I: historic perspectives and current applications. Journal of Endodontics 41, 1778-83.
Ha JH, De-Deus G, Versluis A, Kwak SW, Kim HC (2019) Safe pseudoelastic limit range under torsional loading with Reciproc Blue. International Endodontic Journal 52, 244-9.
Hou X, Yahata Y, Hayashi Y, Ebihara A, Hanawa T, Suda H (2011) Phase transformation behaviour and bending property of twisted nickel - titanium endodontic instruments. International Endodontic Journal 44, 253-8.
Iacono F, Pirani C, Generali L et al. (2016) Wear analysis and cyclic fatigue resistance of electro discharge machined NiTi rotary instruments. Giornale Italiano di Endodonzia 30, 64-8.
Iacono F, Pirani C, Generali L et al. (2017) Structural analysis of HyFlex EDM instruments. International Endodontic Journal 50, 303-13.
IARC International Agency for Research on Cancer (2010). IARC monographs on the evaluation of carcinogenic risks to humans, volume 93. Carbon Black, Titanium Dioxide, and Talc. Lyon, France: World Health Organization.
Inan U, Aydin C, Tunca YM (2007) Cyclic fatigue of ProTaper rotary nickel-titanium instruments in artificial canals with 2 different radii of curvature. Oral Surgery Oral Medicine Oral Pathology Oral Radiology and Endodontics 104, 837-40.
Inan U, Aydin C, Demirkaya K (2011) Cyclic fatigue resistance of new and used Mtwo rotary nickel-titanium instruments in two different radii of curvature. Australian Endodontic Journal 37, 105-8.
Inan U, Keskin C, Sivas Yilmaz Ö, Baş G (2018) Cyclic fatigue of Reciproc Blue and Reciproc instruments exposed to intracanal temperature in simulated severe apical curvature. Clinical Oral Investigation 23, 2077-82. https://doi.org/10.1007/s00784-018-2631-7.
International Organization for Standardization ISO 3630-1. Dental root canal instruments: part 1-files, reamers, barbed broaches, rasps, paste carriers, explorers and cotton broaches. Geneva, Switzerland: International Organization for Standardization; 1992.
Keskin C, Inan U, Demirai M, Keleş A (2017) Cyclic Fatigue Resistance of Reciproc Blue, Reciproc, and WaveOne Gold Reciprocating Instruments. Journal of Endodontics 43, 1360-3.
Kosti E, Zinelis S, Molyvdas I, Lambrianidis T (2011) Effect of root canal curvature on the failure incidence of ProFile royary Ni-Ti endodontic instruments. International Endodontic Journal 44, 917-25.
Liu J (2009) Characterization of new rotary endodontic instruments fabricated from special thermomechanically processed NiTi wire (PhD Thesis). Ohio, USA. The Ohio State University.
Losertovà M, Štencek M, Matýsek D, Štefek O, Drápala J (2017) Microstructure evolution of heat trated NiTi alloys. IOP Conference Series: Materials Sciences and Engineering 266, 012008.
Magalhães RR, Braga LC, Pereira ÉS, Peixoto IF, Buono VT, Bahia MG (2016) The impact of clinical use on the torsional behavior of Reciproc and WaveOne instruments. Journal of Applied Oral Science 24, 310-6.
Murray JL (1987) Phase diagrams of binary titanium alloys. In: Murray JL, ed. Metals Park. ASM International: OH, USA, pp 12-24.
Ninan E, Berzins DW (2013) Torsion and bending properties of shape memory and superelastic nickel-titanium rotary instruments. Journal of Endodontics 39, 101-4.
Oliver WC, Pharr GM (1992) An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. Journal of Materials Research 7, 1564-83.
Özyürek T (2016) Cyclic fatigue resistance of Reciproc, WaveOne, and WaveOne gold nickel-titanium instruments. Journal of Endodontics 42, 1536-9.
Panitvisai P, Parunnit P, Sathorn C, Messer HH (2010) Impact of a retained instrument on treatment outcome : a systematic review and meta-analysis. Journal of Endodontics 36, 775-80.
Park SY, Cheung GS, Yum J, Hur B, Park JK, Kim HC (2010) Dynamic torsional resistance of nickel-titanium rotary instruments. Journal of Endodontics 36, 1200-4.
Pedullà E, Grande NM, Plotino G, Gambarini G, Rapisarda E (2013) Influence of continuous or Reciprocating motion on cyclic fatigue resistance of 4 different nickel-titanium rotary instruments. Journal of Endodontics 39, 258-61.
Pedullà E, Lo Savio F, Boninelli S et al. (2015) Influence of cyclic torsional preloading on cyclic fatigue resistance of nickel - titanium instruments. International Endodontic Journal 48, 1043-50.
Pedullà E, Benites A, La Rosa GM et al. (2018) Cyclic fatigue resistance of heat-treated nickel-titanium instruments after immersion in sodium hypochlorite and/or sterilization. Journal of Endodontics 44, 648-53.
Pérez P, Salmi G, Muñoz A, Monge MA (2009) Influence of yttria additions on the oxidation behaviour of titanium prepared by powder metallurgy. Scripta Materialia 60, 1008-11.
Peters OA (2004) Current challenges and concepts in the preparation of root canal systems: a review. Journal of Endodontics 30, 559-67.
Peters OA, Barbakow F (2002) Dynamic torque and apical forces of ProFile .04 rotary instruments during preparation of curved canals. International Endodontic Journal 35, 379-89.
Pirani C, Ruggeri O, Cirulli P, Pelliccioni GA, Gandolfi MG, Prati C (2014) Metallurgical analysis and fatigue resistance of WaveOne and ProTaper nickel-titanium instruments. Odontology 102, 211-6.
Pirani C, Iacono F, Generali L et al. (2016) HyFlex EDM: superficial features, metallurgical analysis and fatigue resistance of innovative electro discharge machined NiTi rotary instruments. International Endodontic Journal 49, 483-93.
Plotino G, Grande NM, Testarelli L et al. (2018) Cyclic fatigue of Reciproc and Reciproc Blue nickel-titanium Reciprocating files at different environmental temperatures. Journal of Endodontics 44, 1549-52.
Pruett JP, Clement DJ, Carnes DL Jr (1997) Cyclic fatigue testing of nickel-titanium endodontic instruments. Journal of Endodontics 23, 77-85.
Silva EJNL, Hecksher F, Antunes HDS, De-Deus G, Elias CN, Vieira VTL (2018) Torsional Fatigue Resistance of Blue-treated Reciprocating Instruments. Journal of Endodontics 44, 1038-41.
Topçuoğlu HS, Topçuoğlu G (2017) Cyclic Fatigue Resistance of Reciproc Blue and Reciproc Files in an S-shaped Canal. Journal of Endodontics 43, 1679-82.
Undisz A, Reuther K, Reuther H, Rettenmayr M (2011) Occurrence and origin of non-martensitic acicular artefacts on NiTi. Acta Materialia 59, 216-24.
Vieira EP, Nakagawa RK, Buono VT, Bahia MG (2009) Torsional behaviour of rotary NiTi ProTaper Universal instruments after multiple clinical use. International Endodontic Journal 42, 947-53.
Wycoff RC, Berzins DW (2012) An in vitro comparison of torsional stress properties of three different rotary nickel-titanium files with a similar cross-sectional design. Journal of Endodontics 38, 1118-20.
Xu X, Eng M, Zheng Y, Eng D (2006) Comparative study of torsional and bending properties for six models of nickel-titanium root canal instruments with different cross-sections. Journal of Endodontics 32, 372-5.
Zhou HM, Shen Y, Zheng W, Li L, Zheng YF, Haapasalo M (2012) Mechanical properties of controlled memory and superelastic nickel-titanium wires used in the manufacture of rotary endodontic instruments. Journal of Endodontics 38, 1535-40.
Zinelis S, Darabara M, Takase T, Ogane K, Papadimitriou GD (2007) The effect of thermal treatment on the resistance of nickel-titanium rotary files in cyclic fatigue. Oral Surgery Oral Medicine Oral Pathology Oral Radiology and Endodontology 103, 843-7.
Zupanc J, Vahdat-Pajouh N, Schäfer E (2018) New thermomechanically treated NiTi alloys - a review. International Endodontic Journal 10, 1088-03.