3D microtissue-derived human stem cells seeded on electrospun nanocomposites under shear stress: Modulation of gene expression.

Different microenvironments trigger distinct differentiation of stem cells. Even without chemical supplementation, mechanical stimulation by shear stress may help to induce the desired differentiation. The cell format, such as three-dimensional (3D) microtissues (MTs), MT-derived cells or single cells (SCs), may have a pivotal impact as well. Here, we studied modulation of gene expression in human adipose-derived stem cells (ASCs) exposed to shear stress and/or after MT formation. Electrospun meshes of poly-lactic-co-glycolic acid and amorphous calcium phosphate nanoparticles (PLGA/aCaP) at a weight ratio of 60:40 were seeded with human ASCs as MTs or as SCs and cultured in Dulbecco's modified Eagle's medium without chemical supplementation. After 2 weeks of static culture, the scaffolds were cultured statically for another 2 weeks or placed in a Bose® bioreactor with a flow rate per area of 0.16 mL cm MTs decayed completely within 2 weeks after seeding on PLGA/aCaP. The osteogenic marker gene alkaline phosphatase and the endothelial cell marker gene CD31 were upregulated in MT-derived ASCs compared with SCs. Shear stress realised by fluid flow perfusion upregulated peroxisome proliferator-activated receptor gamma 2 expression in MT-derived ASCs and in SCs. The nuclear-to-cytoplasmic ratio of YAP expression was doubled under perfusion compared with that under static culture for MT-derived ASCs and SCs. Osteogenic and angiogenic commitments were more pronounced in MT-derived ASCs seeded on bone biomimetic electrospun nanocomposite PLGA/aCaP than in SCs seeded without induction medium. Furthermore, the static culture was superior to the perfusion regimen used here, as shear stress resulted in adipogenic commitment for MT-derived ASCs and SCs, although the YAP nuclear-to-cytoplasmic ratio indicated higher cell tensions under perfusion, usually associated with preferred osteogenic differentiation.

Informations de copyright

Copyright © 2019 Elsevier Ltd. All rights reserved.