The effects of vıtal dyes on mechanıcal propertıes of the human anterıor lens capsule.

The purpose of this study was to evaluate the mechanical effects of vital dyes on the anterior lens capsule via the nanoindentation method. Twenty anterior lens capsules of 20 different patients were dissected into four equal fragments. Each fragment was stained separately with dyes for intraocular surgeries, such as trypan blue 0.06% (TB), brilliant blue 0.025% (BB), and indocyanine green 0.05% (ICG), for 1 min. The remaining fragment was assessed as an untreated control group. The alterations on the mechanical characteristics of the anterior lens capsule were evaluated using a nanoindentation testing device with Oliver-Pharr and Martens hardness methods. The mean values of elasticity were 7.842 ± 0.55 GPa for capsules fragments stained with TB (P < 0.05), 8.407 ± 0.82 GPa for capsules fragments stained with BB (P < 0.05), 8.557 ± 0.60 GPa for ICG (P < 0.05), and 6.09 ± 0.57 GPa for the untreated control group. The mean values of stiffness were 299.7 ± 47 MPa for TB (P < 0.05), 317.9 ± 34 MPa for BB (P < 0.05), 331.8 ± 48 MPa for ICG (P < 0.05), and 229.85 ± 44 MPa for the untreated control group. The elasticity of the capsules statistically decreased in comparison to the control group, and the capsule stiffness showed a statistically significant increase in comparison to the untreated controls. The mechanical characteristics of the human anterior lens capsule were affected in association with the alterations in the elasticity and stiffness properties of the capsule as a result of exposure to three different dyes.

Déclaration de conflit d'intérêts

None