The Tensile Properties, Scratch Behaviors and Sliding Wear of Oxide Scale Formed on Titanium Grade 2.
adhesion
isothermal oxidation
oxide layers
tensile properties
titanium
tribological properties
Journal
Materials (Basel, Switzerland)
ISSN: 1996-1944
Titre abrégé: Materials (Basel)
Pays: Switzerland
ID NLM: 101555929
Informations de publication
Date de publication:
08 Jul 2020
08 Jul 2020
Historique:
received:
07
05
2020
revised:
03
07
2020
accepted:
06
07
2020
entrez:
12
7
2020
pubmed:
12
7
2020
medline:
12
7
2020
Statut:
epublish
Résumé
The tensile properties, scratch behaviors and sliding wear of an oxide scale obtained on the surface of titanium Grade 2 in the process of isothermal oxidation at 600, 700 and 800 °C were determined in the study. It was shown that the intensity of the oxidation process increased along with an increase in temperature and extension of the oxidation time, which translated directly into the thickness of the deposited oxide layers. The tests showed that isothermal oxidation had an adverse effect on the tensile properties of titanium. After oxidation, it was found that the maximum reduction in tensile strength, R
Identifiants
pubmed: 32650444
pii: ma13143048
doi: 10.3390/ma13143048
pmc: PMC7411679
pii:
doi:
Types de publication
Journal Article
Langues
eng
Références
Materials (Basel). 2020 Apr 21;13(8):
pubmed: 32326223
J Prosthodont Res. 2019 Jul;63(3):266-270
pubmed: 31147298
Materials (Basel). 2019 Dec 24;13(1):
pubmed: 31878174
Mater Sci Eng C Mater Biol Appl. 2019 May;98:279-287
pubmed: 30813028
Phys Rev Lett. 2009 Jan 30;102(4):045501
pubmed: 19257438