Antimicrobial Activity and Biocompatibility of Antibiotic-Loaded Chitosan Hydrogels as a Potential Scaffold in Regenerative Endodontic Treatment.

The objective of this study was to determine the effectiveness of several antibiotic-loaded hydrogel scaffolds against Enterococcus faecalis, as well as their ability to stimulate proliferation and mineralization of dental pulp stem cells. Fibrin (Fg) or chitosan-fibrin hydrogels (Ch) were prepared using 12.5 mg/mL fibrinogen and 0.4% (w/v) chitosan. Triple antibiotics, clindamycin-modified triple antibiotic paste, or double antibiotics were loaded in gels (1 mg/mL). Antibacterial effect against E. faecalis biofilm was determined by using colony-forming units (CFUs) and confocal laser scanning microscope (CLSM). Cell viability and morphology were determined by loading cells into different gels at 7 and 14 days using the water-soluble tetrazolium salt-1 cell viability assay and Live & Dead cell analysis. Mineralization was detected by using alkaline phosphatase and alizarin red staining activity. Antibiotic-loaded Fg gel and Ch gel alone without antibiotics resulted in a significant reduction in CFUs compared with the positive control (P < .05). When antibiotics were loaded in Ch gel, there were no CFUs detected in any groups (P < .05). CLSM images showed dense red areas with mostly dead bacteria on the dentin surface in antibiotic-loaded Ch groups, which showed significantly less live bacteria compared with the other groups (P < .05). Triple antibiotic-loaded Fg and Ch gels resulted in a dramatic decrease in the mineralized nodule formation compared with all other gel groups (P < .05). Ch hydrogels resulted in round cell morphology up to 7 days. Ch alone or with double antibiotic paste showed more cell spreading with spindle-shaped morphology at 14 days and higher alkaline phosphatase activity compared with other antibiotic-loaded Ch groups (P > .05). Double antibiotic-loaded Ch gel appears to enhance the antibacterial properties while maintaining higher cell viability, cell spreading, and mineralization activity, compared with all the other scaffolds investigated.

Informations de copyright

Published by Elsevier Inc.