Impact on Mechanical Properties of 10 versus 20 Minute Treatment of Human Pericardium with Glutaraldehyde in OZAKI Procedure.

The aim of this study was to analyze the effects of 10-minute (standard term) versus 20-minute treatment with glutaraldehyde (GA) on mechanical stability and physical strength of human pericardium in the setting of the OZAKI procedure. Leftover pericardium (6 patients) was bisected directly after the operation, and one-half was further fixed for 10 additional minutes. Uniaxial tensile tests were performed and ultimate tensile strength (UTS), ultimate tensile strain (uts), and collagen elastic modulus were evaluated. Both treatments resulted in similar values of uniaxial stretching-generated elongations at rupture (10 minutes 25 ± 7 % vs. 20 minutes: 22 ± 5 %; p = 0.05), UTS (5.16 ± 2 MPa vs. 6.54 ± 3 MPa; p = 0.59), and collagen fiber stiffness (elastic modulus: 31.80 ± 15.05 MPa vs. 37.35 ± 15.78 MPa; p = 0.25). Prolongation of the fixation time of autologous pericardium has no significant effect on its mechanical stability; thus, extending the intraoperative treatment cannot be recommended.