Low-profile dual mini-fragment plating of diaphyseal clavicle fractures. A biomechanical comparative testing.
Biomechanics
Clavicle fracture
Dual plating
Implant removal
Symptomatic implants
Journal
Clinical biomechanics (Bristol, Avon)
ISSN: 1879-1271
Titre abrégé: Clin Biomech (Bristol, Avon)
Pays: England
ID NLM: 8611877
Informations de publication
Date de publication:
04 2022
04 2022
Historique:
received:
17
11
2021
revised:
11
03
2022
accepted:
25
03
2022
pubmed:
4
4
2022
medline:
28
4
2022
entrez:
3
4
2022
Statut:
ppublish
Résumé
Implant removal rates after clavicle plating are high. Recently, low-profile dual mini-fragment plate constructs have revealed lower implant removal rates following fixation of diaphyseal clavicle fractures. However, they have not been subject to a biomechanical investigation. To: (1) investigate thebiomechanical competence of different dual plate designs and (2) compare them against single superoanterior plating. Twelve artificial clavicles with a simulated AO/OTA 15.2C unstable diaphyseal clavicle fracture were assigned to 2 groups and instrumented with dual titanium mandible plates as follows: Group 1 - 2.5 mm anterior plus 2.0 mm superior (2.5/2.0); Group 2 - 2.0 mm anterior plus 2.0 mm superior (2.0/2.0). Specimens were cyclically tested to failure under craniocaudal cantilever bending superimposed with torsion around the shaft axis and compared to previous published data acquired using 6 locking superoanterior plates tested under the same conditions (Group 3). Initial stiffness was highest in Group 1 followed by Group 2 and Group 3, being significantly different between Group 1 and Group 3 (p = 0.020). Displacement after 5000 cycles was biggest in Group 3, followed by Group 2 and Group 1, with significant differences between Group 3 and both Group 1 and Group 2 (p ≤ 0.027). Cycles to failure were highest in Group 3 followed by Group 1 and Group 2, being significantly different between Group 2 and Group 3 (p = 0.004). Low-profile 2.0/2.0 dual plates demonstrated similar initial stiffness compared with single 3.5 mm locking plates, however, they revealed significantly lower resistance to failure. Moreover, low-profile 2.5/2.0 dual plates demonstrated significantly higher initial stiffness and similar resistance to failure compared with single 3.5 mm locking plates and can therefore be considered as their useful alternative for diaphyseal clavicle fracture fixation.
Sections du résumé
BACKGROUND
Implant removal rates after clavicle plating are high. Recently, low-profile dual mini-fragment plate constructs have revealed lower implant removal rates following fixation of diaphyseal clavicle fractures. However, they have not been subject to a biomechanical investigation.
AIMS
To: (1) investigate thebiomechanical competence of different dual plate designs and (2) compare them against single superoanterior plating.
METHODS
Twelve artificial clavicles with a simulated AO/OTA 15.2C unstable diaphyseal clavicle fracture were assigned to 2 groups and instrumented with dual titanium mandible plates as follows: Group 1 - 2.5 mm anterior plus 2.0 mm superior (2.5/2.0); Group 2 - 2.0 mm anterior plus 2.0 mm superior (2.0/2.0). Specimens were cyclically tested to failure under craniocaudal cantilever bending superimposed with torsion around the shaft axis and compared to previous published data acquired using 6 locking superoanterior plates tested under the same conditions (Group 3).
FINDINGS
Initial stiffness was highest in Group 1 followed by Group 2 and Group 3, being significantly different between Group 1 and Group 3 (p = 0.020). Displacement after 5000 cycles was biggest in Group 3, followed by Group 2 and Group 1, with significant differences between Group 3 and both Group 1 and Group 2 (p ≤ 0.027). Cycles to failure were highest in Group 3 followed by Group 1 and Group 2, being significantly different between Group 2 and Group 3 (p = 0.004).
INTERPRETATION
Low-profile 2.0/2.0 dual plates demonstrated similar initial stiffness compared with single 3.5 mm locking plates, however, they revealed significantly lower resistance to failure. Moreover, low-profile 2.5/2.0 dual plates demonstrated significantly higher initial stiffness and similar resistance to failure compared with single 3.5 mm locking plates and can therefore be considered as their useful alternative for diaphyseal clavicle fracture fixation.
Identifiants
pubmed: 35367818
pii: S0268-0033(22)00064-X
doi: 10.1016/j.clinbiomech.2022.105634
pii:
doi:
Types de publication
Journal Article
Langues
eng
Sous-ensembles de citation
IM
Pagination
105634Informations de copyright
Copyright © 2022 Elsevier Ltd. All rights reserved.