Influence of Resorcinol to Sodium Carbonate Ratio on Carbon Xerogel Properties for Aluminium Ion Battery.
Raman
X-ray diffraction
aluminium-ion battery
carbon
conductivity
intercalation
pseudo-capacitance
resorcinol
soft-template
xerogel
Journal
Materials (Basel, Switzerland)
ISSN: 1996-1944
Titre abrégé: Materials (Basel)
Pays: Switzerland
ID NLM: 101555929
Informations de publication
Date de publication:
01 Apr 2022
01 Apr 2022
Historique:
received:
26
02
2022
revised:
29
03
2022
accepted:
30
03
2022
entrez:
12
4
2022
pubmed:
13
4
2022
medline:
13
4
2022
Statut:
epublish
Résumé
Carbon xerogels were synthesized using a soft-template route with resorcinol as the carbon source and sodium carbonate as the catalyst. The influence of the resorcinol to catalyst ratio in the range of 500-20,000 on pore structure, graphitic domains, and electronic conductivity of as-prepared carbon xerogels, as well as their performance in an aluminium ion battery (AIB), was investigated. After carbonization steps of the polymers up to 800 °C, all carbon samples exhibited similar specific volumes of micropores (0.7-0.8 cm³ g
Identifiants
pubmed: 35407929
pii: ma15072597
doi: 10.3390/ma15072597
pmc: PMC9000357
pii:
doi:
Types de publication
Journal Article
Langues
eng
Subventions
Organisme : Federal Ministry of Education and Research
ID : 03XP0128D
Références
Phys Rev B Condens Matter. 1995 Oct 1;52(14):10053-10059
pubmed: 9980051
ACS Nano. 2018 Aug 28;12(8):8456-8466
pubmed: 30048113
Materials (Basel). 2019 Dec 26;13(1):
pubmed: 31887992
Chem Soc Rev. 2018 Apr 23;47(8):2680-2721
pubmed: 29577123
Phys Chem Chem Phys. 2017 Mar 15;19(11):7980-7989
pubmed: 28263339
Phys Chem Chem Phys. 2020 Mar 11;22(10):5969-5975
pubmed: 32123887
Proc Natl Acad Sci U S A. 2018 May 29;115(22):5670-5675
pubmed: 29760096
Adv Mater. 2018 May;30(20):e1800533
pubmed: 29602214
Angew Chem Int Ed Engl. 2018 Dec 17;57(51):16606-16617
pubmed: 29566301
Nature. 2015 Apr 16;520(7547):325-8
pubmed: 25849777
Philos Trans A Math Phys Eng Sci. 2004 Nov 15;362(1824):2271-88
pubmed: 15482979
Angew Chem Int Ed Engl. 2014 Sep 15;53(38):10169-73
pubmed: 25056756
Nat Commun. 2017 Feb 13;8:14283
pubmed: 28194027
ACS Appl Mater Interfaces. 2017 Aug 30;9(34):28478-28485
pubmed: 28766336
Small. 2018 Dec;14(51):e1803584
pubmed: 30358077
Chem Commun (Camb). 2018 Apr 19;54(33):4164-4167
pubmed: 29629443
J Am Chem Soc. 2012 Dec 19;134(50):20457-65
pubmed: 23190415
Adv Mater. 2017 Jan;29(4):
pubmed: 27859684
Nano Lett. 2011 Aug 10;11(8):3190-6
pubmed: 21696186
Science. 1995 Jun 9;268(5216):1466-8
pubmed: 17843666
ACS Appl Mater Interfaces. 2017 Oct 25;9(42):36702-36707
pubmed: 28972779
Sci Adv. 2017 Dec 15;3(12):eaao7233
pubmed: 29255803