Synthesis and characterization of hydroxyl-terminated butadiene-end-capped polyisobutylene and its use as a diol for polyurethane preparation.

Journal

RSC advances
ISSN: 2046-2069
Titre abrégé: RSC Adv
Pays: England
ID NLM: 101581657

Informations de publication

Date de publication:
02 Mar 2020
Historique:
received: 06 01 2020
accepted: 16 02 2020
entrez: 2 5 2022
pubmed: 5 3 2020
medline: 5 3 2020
Statut: epublish

Résumé

Hydroxyl-terminated telechelic polyisobutylene (PIB) was prepared through living cationic polymerization. A living PIB chain was formed using the

Identifiants

DOI: 10.1039/d0ra00132e PMID: 35497236 PMC: PMC9050137
pubmed: 35497236
doi: 10.1039/d0ra00132e
pii: d0ra00132e
pmc: PMC9050137
doi:

Types de publication

Journal Article

Langues

eng

Pagination

9601-9609

Informations de copyright

This journal is © The Royal Society of Chemistry.

Déclaration de conflit d'intérêts

There are no conflicts to declare.

Références

Langmuir. 2011 Dec 6;27(23):14160-8
pubmed: 22023013
J Chromatogr A. 2015 Jan 9;1376:98-104
pubmed: 25533396

Auteurs

Kangda Wu (K)

Beijing Key Lab of Special Elastomeric Composite Materials, Department of Materials Science and Engineering, Beijing Institute of Petrochemical Technology Beijing 102617 China biptwkd@163.com wangh@bipt.edu.cn shangyuwei@bipt.edu.cn lishuxin@bipt.edu.cn wuyibo@bipt.edu.cn.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Yibo Wu (Y)

Beijing Key Lab of Special Elastomeric Composite Materials, Department of Materials Science and Engineering, Beijing Institute of Petrochemical Technology Beijing 102617 China biptwkd@163.com wangh@bipt.edu.cn shangyuwei@bipt.edu.cn lishuxin@bipt.edu.cn wuyibo@bipt.edu.cn.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.
ORCID: 0000-0002-3739-4643

Shan Huang (S)

College of Material Science and Engineering, Beijing University of Chemical Technology Beijing 100029 China h18811044437@163.com chenzhifei1615@163.com.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Zhifei Chen (Z)

College of Material Science and Engineering, Beijing University of Chemical Technology Beijing 100029 China h18811044437@163.com chenzhifei1615@163.com.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Hao Wang (H)

Beijing Key Lab of Special Elastomeric Composite Materials, Department of Materials Science and Engineering, Beijing Institute of Petrochemical Technology Beijing 102617 China biptwkd@163.com wangh@bipt.edu.cn shangyuwei@bipt.edu.cn lishuxin@bipt.edu.cn wuyibo@bipt.edu.cn.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Yuwei Shang (Y)

Beijing Key Lab of Special Elastomeric Composite Materials, Department of Materials Science and Engineering, Beijing Institute of Petrochemical Technology Beijing 102617 China biptwkd@163.com wangh@bipt.edu.cn shangyuwei@bipt.edu.cn lishuxin@bipt.edu.cn wuyibo@bipt.edu.cn.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Shuxin Li (S)

Beijing Key Lab of Special Elastomeric Composite Materials, Department of Materials Science and Engineering, Beijing Institute of Petrochemical Technology Beijing 102617 China biptwkd@163.com wangh@bipt.edu.cn shangyuwei@bipt.edu.cn lishuxin@bipt.edu.cn wuyibo@bipt.edu.cn.
Beijing Key Lab of Special Elastomeric Composite Materials Beijing 102617 China.

Classifications MeSH