A case-driven hypothesis for multi-stage crack growth mechanism in fourth-generation ceramic head fracture.
Ceramic bearing
Ceramic head fracture
Fracture rate
Hip prosthesis
Mode of failure
Journal
Journal of orthopaedic surgery and research
ISSN: 1749-799X
Titre abrégé: J Orthop Surg Res
Pays: England
ID NLM: 101265112
Informations de publication
Date de publication:
03 Jun 2022
03 Jun 2022
Historique:
received:
07
04
2022
accepted:
13
05
2022
entrez:
6
6
2022
pubmed:
7
6
2022
medline:
9
6
2022
Statut:
epublish
Résumé
Ceramic bearings are used in total hip arthroplasty due to their excellent wear behaviour and biocompatibility. The major concern related to their use is material brittleness, which significantly impacts on the risk of fracture of ceramic components. Fracture toughness improvement has contributed to the decrease in fracture rate, at least of the prosthetic head. However, the root cause behind these rare events is not fully understood. This study evaluated head fracture occurrence in a sizeable cohort of patients with fourth-generation ceramic-on-ceramic implants and described the circumstances reported by patients in the rare cases of head fracture. The clinical survivorship of 29,495 hip prostheses, with fourth-generation ceramic bearings, was determined using data from a joint replacement registry. The average follow-up period was 5.2 years (range 0.1-15.6). Retrieval analysis was performed in one case for which the ceramic components were available. Clinical outcomes confirmed the extremely low fracture rate of fourth-generation ceramic heads: only two out of 29,495 heads fractured. The two fractures, both involving 36 mm heads, occurred without a concurrent or previous remarkable trauma. Considering the feature of the fractured head, a multi-stage crack growth mechanism has been hypothesized to occur following damage at the head-neck taper interface. Surgeons must continue to pay attention to the assembly of the femoral head: achieving a proper head seating on a clean taper is a prerequisite to decrease the risk of occurrence of any damage process within head-neck junction, which may cause high stress concentration at the contact surface, promoting crack nucleation and propagation even in toughened ceramics.
Sections du résumé
BACKGROUND
BACKGROUND
Ceramic bearings are used in total hip arthroplasty due to their excellent wear behaviour and biocompatibility. The major concern related to their use is material brittleness, which significantly impacts on the risk of fracture of ceramic components. Fracture toughness improvement has contributed to the decrease in fracture rate, at least of the prosthetic head. However, the root cause behind these rare events is not fully understood. This study evaluated head fracture occurrence in a sizeable cohort of patients with fourth-generation ceramic-on-ceramic implants and described the circumstances reported by patients in the rare cases of head fracture.
METHODS
METHODS
The clinical survivorship of 29,495 hip prostheses, with fourth-generation ceramic bearings, was determined using data from a joint replacement registry. The average follow-up period was 5.2 years (range 0.1-15.6). Retrieval analysis was performed in one case for which the ceramic components were available.
RESULTS
RESULTS
Clinical outcomes confirmed the extremely low fracture rate of fourth-generation ceramic heads: only two out of 29,495 heads fractured. The two fractures, both involving 36 mm heads, occurred without a concurrent or previous remarkable trauma. Considering the feature of the fractured head, a multi-stage crack growth mechanism has been hypothesized to occur following damage at the head-neck taper interface.
CONCLUSIONS
CONCLUSIONS
Surgeons must continue to pay attention to the assembly of the femoral head: achieving a proper head seating on a clean taper is a prerequisite to decrease the risk of occurrence of any damage process within head-neck junction, which may cause high stress concentration at the contact surface, promoting crack nucleation and propagation even in toughened ceramics.
Identifiants
pubmed: 35658905
doi: 10.1186/s13018-022-03190-6
pii: 10.1186/s13018-022-03190-6
pmc: PMC9164427
doi:
Types de publication
Journal Article
Langues
eng
Sous-ensembles de citation
IM
Pagination
293Informations de copyright
© 2022. The Author(s).
Références
J Arthroplasty. 2017 Feb;32(2):546-551
pubmed: 27623429
JBJS Case Connect. 2019 Dec;9(4):e0336
pubmed: 31592818
J Orthop Res. 2018 Jun;36(6):1630-1636
pubmed: 29319895
Clin Orthop Relat Res. 1996 Jul;(328):129-36
pubmed: 8653945
J Bone Joint Surg Am. 2008 Feb;90(2):329-36
pubmed: 18245593
Open Orthop J. 2012;6:362-5
pubmed: 22927896
J Arthroplasty. 2002 Jun;17(4):503-4
pubmed: 12066284
Emerg Radiol. 2015 Apr;22(2):211-4
pubmed: 25491939
Arthroplast Today. 2021 Aug 05;10:144-148
pubmed: 34401417
Clin Orthop Relat Res. 2015 Dec;473(12):3762-9
pubmed: 26054482
Materials (Basel). 2017 Jul 01;10(7):
pubmed: 28773095
JBJS Case Connect. 2013 Jul-Sep;3(3):e76
pubmed: 29252615
Clin Orthop Relat Res. 2016 Apr;474(4):985-94
pubmed: 26847452
J Arthroplasty. 2008 Dec;23(8):1239.e25-30
pubmed: 18534489
Orthopedics. 2018 Nov 1;41(6):e880-e883
pubmed: 30125036
Int J Artif Organs. 2006 Aug;29(8):800-8
pubmed: 16969758
J Biomed Mater Res B Appl Biomater. 2018 Jul;106(5):1897-1906
pubmed: 28941162
J Biomed Mater Res B Appl Biomater. 2010 Nov;95(2):263-8
pubmed: 20860044
Orthop Traumatol Surg Res. 2014 Oct;100(6 Suppl):S317-21
pubmed: 25130763
J Biomech. 2014 May 7;47(7):1634-41
pubmed: 24657104
Biomaterials. 2002 Feb;23(3):937-45
pubmed: 11774853
Proc Inst Mech Eng H. 2013 May;227(5):535-42
pubmed: 23637263
JBJS Case Connect. 2015 Oct-Dec;5(4):e112
pubmed: 29252818
Bone Joint J. 2017 Aug;99-B(8):1012-1019
pubmed: 28768777
J Arthroplasty. 2015 Sep;30(9 Suppl):110-5
pubmed: 26122108
Clin Orthop Relat Res. 2013 Oct;471(10):3270-82
pubmed: 23761174
Tribol Int. 2017 Sep;113:323-329
pubmed: 28867870
JBJS Case Connect. 2014 Oct/Dec/Nov;4(4):e97
pubmed: 29252765
BMC Musculoskelet Disord. 2019 May 30;20(1):263
pubmed: 31142296
J Mech Behav Biomed Mater. 2014 Mar;31:107-16
pubmed: 23746930
Clin Orthop Relat Res. 2016 Oct;474(10):2190-9
pubmed: 27255729