Evaluation of Degree of Conversion, Resin-Dentin Bond Strength, and Durability of Polydopamine Incorporated Total Etch Adhesive System.
3M Single Bond Dental Adhesive
Dental Bonding
Dental Etching
Polydopamine
Polymerization
Journal
Frontiers in dentistry
ISSN: 2676-296X
Titre abrégé: Front Dent
Pays: Iran
ID NLM: 101747773
Informations de publication
Date de publication:
2020
2020
Historique:
received:
21
03
2018
accepted:
04
11
2020
entrez:
31
8
2022
pubmed:
17
12
2020
medline:
17
12
2020
Statut:
epublish
Résumé
This study aimed to evaluate the degree of conversion (DC%), shear bond strength (SBS), bond durability, and the resin-dentin interface of polydopamine (PDA) incorporated total-etch adhesive system. Five percentage by weight (wt%) concentration of PDA incorporated adhesive was prepared and its polymerization was evaluated using Fourier-transform infrared spectroscopy. The results were compared with the DC% of conventional total-etch adhesive (Adper Single Bond 2) using independent t-test. Occlusal surfaces of 80 freshly extracted human premolars were sectioned to expose the dentin, which was acid-etched. The samples were divided into two groups (n=40) of total-etch adhesive and total-etch adhesive+PDA. Composite resin blocks were built up over the bonded surface and cured. Each group was subdivided into two subgroups (n=20) of immediate and post-aging evaluation. Samples were immersed in 10% sodium hypochlorite for five hours, and then, the SBS was evaluated using a universal testing machine at a crosshead speed of 1 mm/minute. The resin-dentin interface was evaluated using confocal laser scanning microscopy. Data were analyzed using two-way analysis of variance and post-hoc Bonferroni test. DC% was not affected by the addition of 5% PDA to the adhesive (group 2). The SBS of group 2A was significantly higher than that of group 1A. There was no significant reduction of SBS in group 2B. The hybrid layer was less degraded after aging in group 2B compared to group 2A. PDA incorporated adhesive increased the immediate bond strength and durability without changing the DC%.
Identifiants
pubmed: 36042804
doi: 10.18502/fid.v17i35.5199
pii: fid-17-35
pmc: PMC9375104
doi:
Types de publication
Journal Article
Langues
eng
Pagination
35Informations de copyright
Copyright © 2020 The Authors. Published by Tehran University of Medical Sciences.
Déclaration de conflit d'intérêts
CONFLICT OF INTEREST STATEMENT None declared.
Références
Pigment Cell Res. 2000 Jun;13(3):179-84
pubmed: 10885677
J Biomed Mater Res A. 2006 Apr;77(1):128-35
pubmed: 16392135
J Biomed Mater Res B Appl Biomater. 2005 Jan 15;72(1):109-16
pubmed: 15389491
ACS Appl Mater Interfaces. 2012 Dec;4(12):6901-10
pubmed: 23176019
Biochemistry. 2001 Mar 6;40(9):2887-93
pubmed: 11258900
Zhonghua Kou Qiang Yi Xue Za Zhi. 2015 Mar;50(3):186-9
pubmed: 26081862
Indian J Dent Res. 2016 Nov-Dec;27(6):652-656
pubmed: 28169265
J Contemp Dent Pract. 2012 Jul 01;13(4):464-71
pubmed: 23151694
J Biomed Nanotechnol. 2014 Oct;10(10):3063-84
pubmed: 25992429
Science. 2007 Oct 19;318(5849):426-30
pubmed: 17947576
J Dent Res. 2000 Jun;79(6):1385-91
pubmed: 10890717
Oper Dent. 2004 Nov-Dec;29(6):705-12
pubmed: 15646228
Biomaterials. 2012 Nov;33(32):7972-83
pubmed: 22902057
Proc Natl Acad Sci U S A. 2006 Aug 29;103(35):12999-3003
pubmed: 16920796
J Biomed Mater Res. 2002 Jan;59(1):46-55
pubmed: 11745536
J Dent Res. 2011 Aug;90(8):953-68
pubmed: 21220360
Biomacromolecules. 2015 Aug 10;16(8):2265-75
pubmed: 26176305
J Dent Res. 2003 Feb;82(2):141-5
pubmed: 12562889
J Am Chem Soc. 2003 Apr 9;125(14):4253-8
pubmed: 12670247
Molecules. 2014 Oct 17;19(10):16779-93
pubmed: 25329871
Dent Mater J. 1999 Mar;18(1):11-8
pubmed: 10786144
Annu Rev Mater Res. 2011 Aug 1;41:99-132
pubmed: 22058660
J Adhes Dent. 1999 Autumn;1(3):211-8
pubmed: 11725669
Biochemistry. 2000 Sep 12;39(36):11147-53
pubmed: 10998254
Aust Dent J. 2011 Jun;56 Suppl 1:31-44
pubmed: 21564114
J Dent Res. 2009 Dec;88(12):1101-6
pubmed: 19861692
J Clin Exp Dent. 2015 Apr 01;7(2):e243-9
pubmed: 26155340
J Esthet Restor Dent. 2007;19(6):340-53; discussion 354
pubmed: 18005284
Biomaterials. 2006 Sep;27(25):4470-6
pubmed: 16687171