Composition-dependent photoconductivities in indium aluminium nitride nanorods grown by magnetron sputter epitaxy.
Journal
Nanoscale advances
ISSN: 2516-0230
Titre abrégé: Nanoscale Adv
Pays: England
ID NLM: 101738708
Informations de publication
Date de publication:
08 Nov 2022
08 Nov 2022
Historique:
received:
15
07
2022
accepted:
29
09
2022
entrez:
16
11
2022
pubmed:
17
11
2022
medline:
17
11
2022
Statut:
epublish
Résumé
Photoconduction (PC) properties were investigated for ternary indium aluminium nitride (In
Identifiants
pubmed: 36381504
doi: 10.1039/d2na00456a
pii: d2na00456a
pmc: PMC9642355
doi:
Types de publication
Journal Article
Langues
eng
Pagination
4886-4894Informations de copyright
This journal is © The Royal Society of Chemistry.
Déclaration de conflit d'intérêts
The authors declare that there are no conflicts of interest to disclose.
Références
Nanoscale. 2017 Oct 5;9(38):14703-14709
pubmed: 28944816
Nano Lett. 2012 Jan 11;12(1):172-6
pubmed: 22142411
Phys Rev Lett. 2006 Mar 31;96(12):125505
pubmed: 16605926
Nanotechnology. 2015 May 29;26(21):215602
pubmed: 25944838
Eur Phys J Plus. 2022;137(7):771
pubmed: 35813181
Nanoscale Res Lett. 2014 May 01;9(1):204
pubmed: 24855462
ACS Appl Mater Interfaces. 2018 Feb 14;10(6):5740-5749
pubmed: 29381044
Nanotechnology. 2020 Nov 13;31(46):465201
pubmed: 32845871
Nanoscale. 2015 Dec 7;7(45):18964-70
pubmed: 26511167
Nat Commun. 2018 Apr 12;9(1):1442
pubmed: 29650960
Nanotechnology. 2018 Nov 16;29(46):464002
pubmed: 30179161
Opt Lett. 2021 Jul 1;46(13):3271-3274
pubmed: 34197433
ACS Appl Mater Interfaces. 2021 Nov 17;13(45):54486-54496
pubmed: 34730933