Microstructure and Corrosion Behavior of ZnAl12Mg3Si0.3 Double-Batch Hot-Dip Coatings.
ZnAlMgSi coatings
corrosion resistance
double hot-dip method
hot-dip galvanizing
Journal
Materials (Basel, Switzerland)
ISSN: 1996-1944
Titre abrégé: Materials (Basel)
Pays: Switzerland
ID NLM: 101555929
Informations de publication
Date de publication:
08 Mar 2023
08 Mar 2023
Historique:
received:
05
02
2023
revised:
25
02
2023
accepted:
06
03
2023
medline:
30
3
2023
entrez:
29
3
2023
pubmed:
30
3
2023
Statut:
epublish
Résumé
This article presents the microstructure (SEM) and corrosion behavior of ZnAl12Mg3Si0.3 (ZAMS) coatings obtained by the double hot-dip method on Sebisty steel with increased strength. On the basis of chemical composition studies in micro-areas (EDS) and phase composition studies (XRD), structural components of the coating and corrosion products formed on the coating surface after exposure to the neutral salt spray (NSS) test (EN ISO 9227) were identified. The presence of the Fe(Al,Si,Zn)
Identifiants
pubmed: 36984042
pii: ma16062162
doi: 10.3390/ma16062162
pmc: PMC10052979
pii:
doi:
Types de publication
Journal Article
Langues
eng
Références
Materials (Basel). 2019 Apr 29;12(9):
pubmed: 31032815
Materials (Basel). 2021 Sep 10;14(18):
pubmed: 34576440
Materials (Basel). 2022 Sep 28;15(19):
pubmed: 36234070