Corrosion Activity of Stainless Steel SS430 and Carbon Steel B450C in a Sodium Silicate Modified Limestone-Portland Cement Extract.
EIS
Portland cement
SEM-EDS
XPS
alkali-activated cement
carbon steel
cement extract solution
corrosion
corrosion potential
pH
stainless steel
Journal
Materials (Basel, Switzerland)
ISSN: 1996-1944
Titre abrégé: Materials (Basel)
Pays: Switzerland
ID NLM: 101555929
Informations de publication
Date de publication:
18 Jul 2023
18 Jul 2023
Historique:
received:
01
06
2023
revised:
29
06
2023
accepted:
10
07
2023
medline:
29
7
2023
pubmed:
29
7
2023
entrez:
29
7
2023
Statut:
epublish
Résumé
Stainless steel SS430 and carbon steel B450C were exposed for 30 days to the aqueous extract of sodium silicate-modified limestone-Portland cement as an alternative for the partial replacement of the Portland cement clinker. The initial pH of 12.60 was lowered and maintained at an average of 9.60, associated with air CO
Identifiants
pubmed: 37512340
pii: ma16145066
doi: 10.3390/ma16145066
pmc: PMC10385683
pii:
doi:
Types de publication
Journal Article
Langues
eng
Références
Materials (Basel). 2023 Mar 11;16(6):
pubmed: 36984140
Materials (Basel). 2021 Nov 25;14(23):
pubmed: 34885324
Materials (Basel). 2022 Nov 07;15(21):
pubmed: 36363440
Materials (Basel). 2022 Oct 22;15(21):
pubmed: 36363001
Materials (Basel). 2022 Dec 08;15(24):
pubmed: 36556588
Materials (Basel). 2022 Nov 03;15(21):
pubmed: 36363356
Data Brief. 2015 Sep 01;5:171-8
pubmed: 26501086
Materials (Basel). 2022 Dec 15;15(24):
pubmed: 36556782
Materials (Basel). 2022 Nov 07;15(21):
pubmed: 36363454
Polymers (Basel). 2022 May 14;14(10):
pubmed: 35631894
Materials (Basel). 2022 Nov 03;15(21):
pubmed: 36363353