Influence of Catalyst Content and Epoxy/Carboxylate Ratio on Isothermal Creep of Epoxy Vitrimers.
compression molding
epoxy matrix
multifunctional composites
vitrimer
Journal
Polymers
ISSN: 2073-4360
Titre abrégé: Polymers (Basel)
Pays: Switzerland
ID NLM: 101545357
Informations de publication
Date de publication:
21 Sep 2023
21 Sep 2023
Historique:
received:
04
08
2023
revised:
16
09
2023
accepted:
19
09
2023
medline:
28
9
2023
pubmed:
28
9
2023
entrez:
28
9
2023
Statut:
epublish
Résumé
In the present work, a commercial epoxy based on epoxy anhydride and tertiary amine was modified by a metallic catalyst (Zn
Identifiants
pubmed: 37765699
pii: polym15183845
doi: 10.3390/polym15183845
pmc: PMC10535981
pii:
doi:
Types de publication
Journal Article
Langues
eng
Subventions
Organisme : Ministry of Economic Development
ID : LAMPO Research Project (CDS00750)
Références
Materials (Basel). 2023 Feb 21;16(5):
pubmed: 36902890
Molecules. 2022 Sep 26;27(19):
pubmed: 36234872
ACS Macro Lett. 2012 Jul 17;1(7):789-792
pubmed: 35607118
Chem Sci. 2016 Jan 1;7(1):30-38
pubmed: 28757995
ACS Macro Lett. 2020 Jun 16;9(6):836-842
pubmed: 35648515
Polymers (Basel). 2022 Dec 14;14(24):
pubmed: 36559840
J Am Chem Soc. 2012 May 9;134(18):7664-7
pubmed: 22537278
Chem Rev. 2023 Mar 22;123(6):3237-3298
pubmed: 36827528
ACS Appl Bio Mater. 2020 Nov 16;3(11):8094-8104
pubmed: 35019549
Science. 2011 Nov 18;334(6058):965-8
pubmed: 22096195
Polymers (Basel). 2019 Jul 31;11(8):
pubmed: 31370297