Biocompatibility and antibacterial activity of MgO/Ca3(PO4)2 composite ceramic scaffold based on vat photopolymerization technology.

Recent advancements in medical technology and increased interdisciplinary research have facilitated the development of the field of medical engineering. Specifically, in bone repair, researchers and potential users have placed greater demands on orthopedic implants regarding their biocompatibility, degradation rates, antibacterial properties, and other aspects. In response, our team developed composite ceramic samples using degradable materials calcium phosphate and magnesium oxide through the vat photopolymerization (VP) technique. The calcium phosphate content in each sample was, respectively, 80 %, 60 %, 40 %, and 20 %. To explore the relationship between the biocompatibility, antibacterial activity, and MgO content of the samples, we cultured them with osteoblasts (MC3T3-E1), Escherichia coli (a gram-negative bacterium), and Staphylococcus aureus (a gram-positive bacterium). Our results demonstrate that as the MgO content of the sample increases, its biocompatibility improves but its antibacterial activity decreases. Regarding the composite material samples, the 20 % calcium phosphate content group exhibited the best biocompatibility. However, after 0.5 h of co-cultivation, the antibacterial rates of all groups except the 20 % calcium phosphate content group co-cultured with S. aureus exceed 80 %. Furthermore, after 3 h, the antibacterial rates against E. coli exceed 95 % in all groups. This is because higher levels of MgO correspond to lower pH values and Mg

Informations de copyright

Copyright © 2023 Elsevier B.V. All rights reserved.

Déclaration de conflit d'intérêts

Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.