Influence of heat input on the mechanical characteristics, corrosion and microstructure of ASTM A36 steel welded by GTAW technique.

The Gas Tungsten Arc Welding process weld for the 4 mm thickness of the ASTM A36 steel plate with varied heat input parameters of 0.608 kJ/mm, 0.900 kJ/mm and 1.466 kJ/mm, respectively. The effect of different heat inputs on microstructure, corrosion, and mechanical characteristics of developed weld joints are examined by three zones: heat-affected zone, welded zone, and base metal zone. The optical microscopic results of weld joints illustrate that fine grain structure leads to enhance welding strength. It is revealed that the increased heat input parameter on the weld joint shows a decreased tensile strength and hardness of the weld joint. The corrosion resistance of the weld joint is evaluated by Potentio-dynamic polarization. It facilitates that the corrosion rate of the weld joint is decreased with increasing heat input, which results indicate the best and worst corrosion micrograph of the polygonal ferrite and ferrite plus polygonal ferrite. However, the weld joint prepared with 0.900 kJ/mm heat input found maximum corrosion resistance.

Informations de copyright

© 2023 Published by Elsevier Ltd.

Déclaration de conflit d'intérêts

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.