Tuning Surface Reactivity and Electric Field Strength via Intermetallic Alloying.
Journal
ACS energy letters
ISSN: 2380-8195
Titre abrégé: ACS Energy Lett
Pays: United States
ID NLM: 101697523
Informations de publication
Date de publication:
13 Oct 2023
13 Oct 2023
Historique:
received:
08
08
2023
accepted:
21
09
2023
medline:
19
10
2023
pubmed:
19
10
2023
entrez:
19
10
2023
Statut:
epublish
Résumé
Many electrosynthesis reactions, such as CO
Identifiants
pubmed: 37854044
doi: 10.1021/acsenergylett.3c01639
pmc: PMC10580307
doi:
Types de publication
Journal Article
Langues
eng
Pagination
4414-4420Informations de copyright
© 2023 The Authors. Published by American Chemical Society.
Déclaration de conflit d'intérêts
The authors declare no competing financial interest.
Références
Chemphyschem. 2019 Nov 19;20(22):2900-2903
pubmed: 31737993
J Am Chem Soc. 2016 Oct 5;138(39):13006-13012
pubmed: 27626299
J Am Chem Soc. 2017 Aug 16;139(32):11277-11287
pubmed: 28738673
ACS Cent Sci. 2016 Aug 24;2(8):522-8
pubmed: 27610413
Proc Natl Acad Sci U S A. 2017 Feb 21;114(8):1795-1800
pubmed: 28167767
J Am Chem Soc. 2017 Nov 15;139(45):16412-16419
pubmed: 29064691
JACS Au. 2022 May 03;2(5):1054-1070
pubmed: 35647596
J Phys Chem Lett. 2015 Jun 4;6(11):2032-7
pubmed: 26266498
Science. 1992 Aug 14;257(5072):897-903
pubmed: 17789634
J Phys Chem Lett. 2016 Apr 21;7(8):1471-7
pubmed: 27045040
J Am Chem Soc. 2014 Oct 8;136(40):14107-13
pubmed: 25259478
Nat Commun. 2019 Jan 3;10(1):32
pubmed: 30604776
Chem Rev. 2019 Jun 26;119(12):7610-7672
pubmed: 31117420
J Am Chem Soc. 2012 Jun 20;134(24):9864-7
pubmed: 22670713
Chemphyschem. 2017 Nov 17;18(22):3266-3273
pubmed: 28872756