Insight into the Li-Storage Property of Surface-Modified Ti
Intercalation anode
carbon−copper coating
lithium-ion battery
oxygen deficiency
titanium niobium oxide
Journal
ACS applied materials & interfaces
ISSN: 1944-8252
Titre abrégé: ACS Appl Mater Interfaces
Pays: United States
ID NLM: 101504991
Informations de publication
Date de publication:
29 Nov 2023
29 Nov 2023
Historique:
medline:
16
11
2023
pubmed:
16
11
2023
entrez:
16
11
2023
Statut:
ppublish
Résumé
Ti-based anode materials are considered to be an alternative to graphite anodes to accomplish high-rate application requirements. Ti
Identifiants
pubmed: 37968909
doi: 10.1021/acsami.3c14174
pmc: PMC10694814
doi:
Types de publication
Journal Article
Langues
eng
Sous-ensembles de citation
IM
Pagination
54568-54581Références
ACS Appl Mater Interfaces. 2018 Jul 18;10(28):23711-23720
pubmed: 29975500
Nat Commun. 2020 Jan 9;11(1):132
pubmed: 31919355
ACS Appl Mater Interfaces. 2013 Feb;5(3):981-8
pubmed: 23323836
ACS Appl Mater Interfaces. 2021 Apr 14;13(14):16445-16453
pubmed: 33793195
Adv Mater. 2010 Dec 14;22(47):5378-82
pubmed: 20949538
Sci Rep. 2018 Apr 25;8(1):6530
pubmed: 29695815
Nat Mater. 2013 Jun;12(6):518-22
pubmed: 23584143
Sci Rep. 2015 Dec 03;5:17836
pubmed: 26632883
J Am Chem Soc. 2019 Oct 23;141(42):16706-16725
pubmed: 31487157
Inorg Chem. 2017 Apr 3;56(7):4002-4010
pubmed: 28319367
Nature. 2018 Jul;559(7715):556-563
pubmed: 30046074