Harnessing oriented arrangement of collagen fibers by 3D printing for enhancing mechanical and osteogenic properties of mineralized collagen scaffolds.

As the structural basis of connective and load-bearing tissues, collagen fibers with orientation play an important role in the mechanical properties and physiological and biochemical functions of the tissues, but viable methods for preparing scaffolds with highly oriented collagenous structure still need to be further studied. In this study, pure collagen was used as printing ink to 3D printing. Harnessing oriented collagen fiber structure by 3D printing for promoting mechanical and osteogenic properties of scaffolds. The scaffolds with different printed angles and thicknesses were prepared to fit the bone defect site and realize personalized customization. The orientation assembly of collagen fibers was promoted by shear force action of 3D printing, the regular arrangement of collagen fibers and stabilization of fiber structure were promoted by pH adjustment and glutaraldehyde cross-linking, and the collagen fibers were mineralized by cyclic mineralization method. The microscopic morphology of fiber arrangement in the scaffolds were investigated by scanning electron microscopy. Results demonstrated that collagen fibers were changed from non-oriented to oriented after 3D printing. And the tensile modulus of the scaffolds with oriented collagen fibers was nine times higher than that of the scaffolds with non-oriented fibers. Moreover, the effects of oriented collagen fibers on the proliferation, differentiation and mineralization of MC3T3-E1 cells were studied by CCK-8 assay, live/dead cell staining, alkaline phosphatase activity test, and Alizarin red staining. The results indicated that cell proliferation, differentiation and mineralization were significantly promoted by oriented collagen fibers, and the cells proliferated directionally in the direction of the fibers. Taken together, mineralized collagen fiber scaffolds with oriented collagen fibers have great potential in bone tissue engineering applications.

Informations de copyright

© 2024 IOP Publishing Ltd.