In-vitro polishing of CAD/CAM ceramic restorations: An evaluation with SEM and confocal profilometry.

The objective of this In-vitro investigation was to analyze and compare the surface after polishing of 63 all-ceramic restorations fabricated out of monolithic zirconium dioxide (ZIR), lithium disilicate (LS) or feldspathic ceramic (FC) under standardized laboratory conditions with different protocols. The primary outcome was defined as the roughness (R The study set-up consisted of three main groups: ZIR, LS, FC (20 crowns each), every group divided into two sub-groups (10 crowns each) depending on the polishing method. The untouched glazed surface of one crown per material served as a control. Every crown displayed a defined supra-contact at the palatal cusp which was removed with a fine grain (38-45 μm) diamond bur. Surface polishing was carried out with either a two-step system (one kit for zirconium dioxide (ZIR Visual examination of the specimens using SEM showed several inhomogeneities on the glazed surface of the control samples, i.e. pores and particles. On every test sample, the grinding curves of the diamond bur were still recognizable. Polishing revealed similar median R The surface roughness of ZIR, LS and FC crowns after the use of chairside polishing kits was comparable with the roughness measured before occlusal adjustment. A two-step procedure showed as good results as a three-step process. A smoother surface was obtained for ZIR and LS compared to FC with both polishing protocols.

Informations de copyright

Copyright © 2020 Elsevier Ltd. All rights reserved.

Déclaration de conflit d'intérêts

Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.