Development of gallic acid-loaded ethylcellulose fibers as a potential wound dressing material.

In this study, novel fibers were designed based on ethylcellulose (EC), loaded with different concentrations of gallic acid (GA) using the electrospinning technique, in order to investigate the potential of these materials as wound dressings. The chemical structure and morphology, along with the antimicrobial and biocompatibility tests of the EC_GA fibers were investigated. To observe the chemical interactions between the components, fourier transform infrared spectroscopy (FTIR) was used. The morphological analyzes were performed using scanning electron microscope (SEM). The uniaxial tensile test machine was used to obtain mechanical performance of the fibers. MTT assay was applied to get the biocompatibility properties of the fibers and antimicrobial test was applied to obtain the antimicrobial activity of the fibers. Based on the obtained results, the highest viability value of 67.4 % was obtained for 10%EC_100GA on the third day of incubation, demonstrating that with the addition of a higher concentration of GA, the cell viability increases. The antimicrobial tests, evaluated against Staphylococcus (S.) aureus, Escherichia (E.) coli, Pseudomonas (Ps.) aeruginosa and Candida (C.) albicans, showed a >90 % microbial reduction capacity correlated with a logarithmic reduction ranging from 0.63 to 1, for 10%EC_100 GA. In vitro release tests of GA from the fibers showed that GA was totally released from 10%EC_100 GA fibers after 2880 min, demonstrating a controlled release profile. These findings demonstrated that EC_GA fibers may be suitable for application in biomedical fields such as wound dressing materials. However, further studies should be performed to increase the biocompatibility properties of the fibers.

Informations de copyright

Copyright © 2023. Published by Elsevier B.V.

Déclaration de conflit d'intérêts

Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.