Effect of ultrasonic activation on setting time, pH and calcium ion release, solubility, and chemical structure of calcium silicate sealers.

This study evaluated the setting time, pH, calcium ion release, solubility, and chemical structure of four calcium silicate sealers after ultrasonic activation (UA). Five sealers were evaluated: Sealer Plus (SP - control); Sealer Plus BC (SPBC), Bio C Sealers (BCS), Endosequence BC Sealer (EBC), and BioRoot RCS (BR). Ten groups were created based on the use or not of ultrasonic activation: SP; SP/UA; SPBC; SPBC/UA; BCS; BCS/UA; EBC; EBC/UA; BR; and BR/UA. Setting time was performed based on ISO 6876:2012 and ASTM C266-07 specifications. Solubility at 24hs, based on ISO 6876:2012. pH and calcium release were evaluated at 1, 24, 72, and 168hs. Raman spectroscopy was used to evaluate structural changes. Quantitative data were analyzed using One-Way ANOVA and Tukey post-hoc test (α=5%). Raman spectroscopy results were qualitatively analyzed. Setting times and solubility of all sealers were not affected by UA (p>0.05). The highest solubility was found for BCS, BCS/UA; and BR, BR/UA (p<0.05). After 24hs, calcium silicate sealers had higher pH than SP and SP/UA (p<0.05). BR and BR/UA had the highest pH at all time points. SP and SP/UA had stable pH at all time points. SP and SP/UA had the lowest calcium release values at all time points (p<0.05). EBC and EBC/UA calcium release significantly differ at 24,72 and 168hs (p<0.05). No chemical changes were observed during Raman spectroscopy. In conclusion, ultrasonic activation affected calcium ion release only for EndoSequence BC Sealer. Ultrasonic activation did not influence the initial and final setting time, solubility, pH, and chemical structure of any investigated sealers.